Product Details
Place of Origin: China
Brand Name: SFT
Model Number: 6900CE
Payment & Shipping Terms
Minimum Order Quantity: negotiable
Price: negotiable
Packaging Details: carton,pallet
Delivery Time: 20-45DAYS
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: 50000PCS/MONTH
Bearing Type: |
Deep Groove |
Vibration: |
V4, V3, V2, V1 |
Content: |
Ceramic |
Application: |
Ceramic Insulating Sleeve |
Cage: |
Steel Cage.copper Cage.nylon Cage |
Product Name: |
Ceramic Ball Bearing |
Bearing Type: |
Deep Groove |
Vibration: |
V4, V3, V2, V1 |
Content: |
Ceramic |
Application: |
Ceramic Insulating Sleeve |
Cage: |
Steel Cage.copper Cage.nylon Cage |
Product Name: |
Ceramic Ball Bearing |
High Temperatures And Corrosive Alumina Zirconia Ceramic Bearings
Full Ceramic Bearings have races and balls that are made entirely of ceramic material and are superior to common steel bearings in many ways. Ceramic is the perfect material for any application seeking to achieve higher RPM’s, reduce overall weight or for extremely harsh environments where high temperatures and corrosive substances are present.
Full Ceramic Bearings are usually made of following materials:
· Silicon Nitride (SiN4)
· Alumina Oxide (Al2O3)
· Zirconia Oxide (ZrO2)
· Silicon Carbide (SiC)
Because ceramic is a glass like surface it has an extremely low coefficient of friction and is ideal for applications seeking to reduce friction.
1. Material peroformance
Full ceramic bearing ZrO2 material
Full ceramic bearing ZrO2 material has great property such like suitable for low and high temperatures, high load capacity, corrosion resistance, nonmagnetic insulated and self lubrication. Thus it suit for the specific applications which are not available for bearing steel and hybrid construction ceramic ball bearing materials.
Full ceramic bearing Si3N4 material
Full ceramic bearing Si3N4 material has similar property as ZrO2
material, In addition; it has lower weight , better wear resistance, high hardness, and it can bear higher temperature than ZrO2 material.
2. Structures
Rings(ZRO2/SI3N4)+ Retainer(PEEK/PTFE/NYLON)+Ball( ZRO2/SI3N4)
Rings(ZRO2/SI3N4) +Ball( ZRO2/SI3N4) full ball without retainer
|
Properties |
Units |
AL2O3 |
ZrO2 |
SiC |
Si3N4 |
|
Density |
g/cm3 |
3.65-3.93 |
5.95-6.0 |
3.12 |
3.23 |
|
Water absorption |
0 |
0 |
0 |
0 |
0 |
|
Poission`s ratio |
/ |
0.21-0.22 |
0.3 |
0.17 |
0.26 |
|
HV hardness hv |
MPa |
1650 |
1300-1365 |
2800 |
1500 |
|
Flexural strength |
MPa |
310 |
950 |
390 |
720 |
|
Heat conductivity |
W/m*k |
26-30 |
2-2.2 |
120 |
25 |
|
Electrical resistivity |
Ω*mm2/m |
>1016 |
>1015 |
>103 |
>1013 |
|
Dielectric constant |
/ |
9.6 |
29 |
9.66-10.03 |
/ |
|
Dielectric strength |
KV/mm |
8.7 |
9 |
/ |
/ |
|
Coefficientof thermal expansion |
10-16/k |
7.9-8.5 |
10.5 |
3 |
3.2 |
|
Modulus of elasticity young`s mod |
GPa |
280-340 |
210 |
440 |
300 |
|
Flexural strength(700℃) |
MPa |
230 |
210 |
380 |
450 |
|
Compressive strength |
MPa |
2200 |
2000 |
1800 |
2300 |
|
Max use temperature |
℃ |
1750 |
1050 |
1550 |
1050 |
|
Resistance to acid alkaline |
/ |
high |
high |
high |
high |
|
Thermal shock resistance |
T(℃) |
180-220 |
280-350 |
230-260 |
/ |
|
Fracture toughness |
MPa*m1/2 |
4.2 |
10 |
3.9 |
6.2 |
|
Tensile strength |
MPa |
248 |
250 |
/ |
/ |